Germanium mediated de-oxidation of silicon

ABSTRACT

A method for removing a native oxide film from a semiconductor substrate includes repetitively depositing layers of germanium on the native oxide and heating the substrate causing the layer of germanium to form germanium oxide, desorbing a portion of the native oxide film. The process is repeated until the oxide film is removed. A subsequent layer of strontium titanate can be deposited on the semiconductor substrate, over either residual germanium or a deposited germanium layer. The germanium can be converted to silicon germanium oxide by exposing the strontium titanate to oxygen.

CROSS-REFERENCES TO OTHER APPLICATIONS

This application claims priority to U.S. provisional patent applicationSer. No. 62/878,653, for “GERMANIUM MEDIATED DE-OXIDATION OF SILICON”filed on Jul. 25, 2019 and to U.S. provisional patent application Ser.No. 62/878,678, for “EPITAXIAL STRONTIUM TITANATE ON SILICON” filed onJul. 25, 2019, which are hereby incorporated by reference in entiretyfor all purposes. This application is related to concurrently filed andcommonly assigned U.S. nonprovisional patent application Ser. No.16/791,914 for “EPITAXIAL STRONTIUM TITANATE ON SILICON” filed on Feb.14, 2020.

FIELD

The described embodiments relate generally to silicon-based wafers forphotonic circuits. More particularly, the present embodiments relate tosilicon wafers that include an epitaxial layer of SrTiO₃,

BACKGROUND

Currently there are a wide variety of methods to remove the nativeoxide, SiO₂, from the surface of a silicon wafer and form an epitaxiallayer of SrTiO₃ on the wafer. Some methods use thermal desorption athigh temperatures of nearly 900° C. or above to remove the amorphousSiO₂ layer on the silicon before depositing one or more layers thatterminate in SrTiO₃. The use of high temperatures often results inexcessive wafer bowing that can be on the order of 100 microns orgreater for an 12 inch wafer. Other methods use one or more hazardouschemicals such as HF to etch the SiO₂, however in addition to beingdangerous, this method often results in

the formation of SiC on the silicon surface which is very difficult toremove and is undesirable for epitaxial growth of SrTiO₃. In addition,semiconductor industry has developed processes that use remote plasma ofNH₃ and NF₃ gas to etch native oxide to form silicate salts that can bethermal desorbed at low-temperatures. Additionally, NH₃ and HF vaporphase reactions have been used to etch native oxide. However, both thesemethods are challenged to leave atomically clean surface of silicon.Further methods use Sr mediated de-oxidation to remove the SiO₂, howeverthere is still an undesirably large lattice mismatch between the siliconand the epitaxial SrTiO₃ layer.

New methods for removing the native oxide from a silicon wafer and forforming an epitaxial SrTiO₃layer on a silicon wafer are needed thatresult in reduced bow of the wafer, increased safety, reduction of theformation of undesirable species on the silicon surface (e.g., SiC) andan improved lattice match between silicon and epitaxial SrTiO₃.

SUMMARY

In some embodiments a method for processing a substrate comprisespositioning the substrate in a deposition chamber, wherein the substratecomprises a wafer of single crystal silicon covered with a layer ofamorphous silicon oxide. A layer of germanium is deposited on the layerof amorphous silicon oxide and the substrate is heated to a temperaturebelow 850° C. causing at least a portion of the layer of amorphoussilicon oxide to react with the layer of germanium to form germaniumoxide.

In some embodiments the method further comprises repeating thedepositing the layer of germanium and the heating the substrate untilthe layer of amorphous silicon oxide is removed from the wafer of singlecrystal silicon. In various embodiments after the amorphous siliconoxide is removed from the wafer of single crystal silicon, residualgermanium from the depositing the layer of germanium is distributed onthe wafer of single crystal silicon. In some embodiments an epitaxiallayer of strontium titanate is deposited on the wafer of single crystalsilicon and on the residual germanium.

In some embodiments the method further comprises exposing the wafer ofsingle crystal silicon to oxygen after the depositing the epitaxiallayer of strontium titanate, causing the silicon and the residualgermanium to react forming a silicon germanium oxide layer between thelayer of strontium titanate and the wafer of single crystal silicon. Invarious embodiments the method further comprises depositing a layer ofgermanium on the wafer of single crystal silicon after the layer ofamorphous silicon oxide is removed. In some embodiments the methodfurther comprises exposing the layer of germanium and the wafer ofsingle crystal silicon to a temperature sufficient to cause the layer ofgermanium to inter-diffuse with the wafer of single crystal silicon tocreate a graded layer having a composition higher in silicon thangermanium at the wafer of single crystal silicon and a composition thatis higher in germanium than silicon at a top of the graded layer.

In some embodiments the method further comprises depositing a gradedlayer on the wafer of single crystal silicon after the layer ofamorphous silicon oxide is removed, wherein the graded layer has acomposition higher in silicon than germanium at the wafer of singlecrystal silicon and a composition that is higher in germanium thansilicon at a top of the graded layer.

In some embodiments a method for removing an oxide layer from asubstrate comprises depositing a layer of germanium on the oxide layerand heating the substrate to a temperature below 850° C. to cause thelayer of germanium to react with the oxide layer and generate germaniumoxide. In various embodiments the substrate comprises silicon and theoxide layer comprises silicon dioxide. In some embodiments the substratecomprises silicon germanium and the oxide layer comprises silicongermanium dioxide. In various embodiments the temperature is between700° C. and 750° C. In some embodiments the method further comprisesrepetitively depositing the layer of germanium and heating the substrateuntil the oxide layer is removed.

In some embodiments the method further comprises depositing germanium ona surface of the substrate after the oxide layer is removed. In variousembodiments the method further comprises depositing an epitaxial layerof strontium titanate after the depositing the germanium. In someembodiments the method further comprises exposing the substrate tooxygen after the depositing the epitaxial layer of strontium titanate,the oxygen causing the germanium to form a layer of silicon germaniumoxide between the substrate and the epitaxial layer of strontiumtitanate.

In some embodiments a method for processing a substrate comprisespositioning the substrate in a deposition chamber, wherein the substratecomprises a top layer of silicon germanium oxide, a middle layer ofsilicon germanium and a bottom layer of silicon. A layer of germanium isdeposited on the layer of silicon germanium oxide and the substrate isheated to a temperature below 850° C. causing at least a portion of thelayer of silicon germanium oxide to react with the layer of germanium toform germanium oxide. In various embodiments the method comprisesrepeating the depositing the layer of germanium and the heating thesubstrate until the layer of silicon germanium oxide is removed from thelayer of silicon germanium.

In some embodiments the method further comprises depositing an epitaxiallayer of strontium titanate on the layer of silicon germanium. Invarious embodiments the method of comprises exposing the layer ofstrontium titanate to oxygen causing the layer of silicon germanium toreact with the oxygen forming a layer of silicon germanium oxide betweenthe layer of strontium titanate and the layer of silicon.

To better understand the nature and advantages of the presentdisclosure, reference should be made to the following description andthe accompanying figures. It is to be understood, however, that each ofthe figures is provided for the purpose of illustration only and is notintended as a definition of the limits of the scope of the presentdisclosure. Also, as a general rule, and unless it is evident to thecontrary from the description, where elements in different figures useidentical reference numbers, the elements are generally either identicalor at least similar in function or purpose.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A-1F illustrates simplified cross-sectional views of steps forforming a SrTiO₃ layer on a silicon wafer, according to embodiments ofthe disclosure;

FIG. 2 is a method for forming a SrTiO₃ layer on a silicon waferaccording to the steps illustrated in FIG. 1;

FIG. 3A-3D illustrates simplified cross-sectional views of steps forforming a SrTiO₃ layer on a silicon wafer, according to embodiments ofthe disclosure;

FIG. 4 is a method for forming a SrTiO₃ layer on a silicon waferaccording to the steps illustrated in FIG. 3;

FIG. 5A-5F illustrates simplified cross-sectional views of steps forforming a SrTiO₃ layer on a silicon wafer that includes a silicongermanium layer, according to embodiments of the disclosure; and

FIG. 6 is a method for forming a SrTiO₃ layer on a silicon waferaccording to the steps illustrated in FIG. 5.

DETAILED DESCRIPTION

Some embodiments of the present disclosure relate to methods for removalof the native oxide from a silicon wafer using Ge mediated de-oxidationand for the subsequent deposition of an epitaxial layer of SrTiO₃. Someembodiments relate to the formation of an intermediate amorphousSi_(1-x)Ge_(x)O₂ layer between the silicon and the SrTiO₃. While thepresent disclosure can be useful for a wide variety of configurations,some embodiments of the disclosure are particularly useful for formingsilicon wafers for use in photonic circuits, as described in more detailbelow.

For example, in some embodiments a silicon wafer includes a layer ofamorphous SiO₂ that must be removed before forming an epitaxial SrTiO₃layer. A first layer of Ge can be deposited on the amorphous SiO₂ andcan react with the SiO₂ when exposed to elevated temperatures in therange of 650-850° C. generating GeO that is volatile and desorbs fromthe Si wafer. This process can be repeated until the Si wafer is freefrom SiO₂, however some residual Ge from the process remains on thesilicon surface. An epitaxial layer of SrTiO₃ can then be formed on thesilicon surface. The wafer can then be exposed to an oxidizingatmosphere to convert the remaining Ge, now disposed between the Si andthe SrTiO₃ layer, to amorphous Si_(1-x)Ge_(x)O₂ which is transparent tocertain wavelengths of laser light.

In another example, after removal of the amorphous SiO₂ from the siliconsurface, a graded layer of Si_(1-x)Ge_(x) can be formed that changesconcentration from a low concentration of Ge at the Si wafer interfaceto a higher concentration of Ge at the top of the graded layer. In someembodiments the graded layer can be formed by depositing a layer of Geand diffusing the Ge into the surface of the Si wafer. In anotherembodiment, the graded layer can be formed by co-evaporating both Si andGe with varying concentrations throughout the epitaxial growth process.A layer of epitaxial SrTiO₃ can then be deposited on the graded layer.

The graded layer can reduce lattice strain between the Si and theSrTiO₃, as the graded layer has a higher concentration of Si at the Siinterface and as such has a relatively close match to the lattice of theSi. Further, the graded layer has a higher concentration of Ge at theSrTiO₃ interface and as such has a relatively close lattice match to theSrTiO₃ layer. Thus the graded layer provides an improved lattice matchbetween the Si and the SrTiO₃ than if the SrTiO₃ were formed directly onthe Si. The graded layer can be subsequently oxidized, converting it toamorphous Si_(1-x)Ge_(x)O₂ which is transparent to certain wavelengthsof laser light.

In another example a Si wafer includes a pregrown epitaxial layer ofSi_(1-x)Ge_(x) that is terminated with a native oxide of SiGeO₂. Gemediated de-oxidation can be used as described above, where a layer ofGe can be deposited on the SiGeO₂ and exposed to a high temperature todesorb the SiGeO₂ layer. Epitaxial SrTiO₃ can be deposited on theSi_(1-x)Ge_(x) layer and the wafer can be exposed to an oxidizingatmosphere to transform the intermediate Si_(1-x)Ge_(x) layer toSi_(1-x)Ge_(x)O₂.

In order to better appreciate the features and aspects of removingnative oxide layers and forming epitaxial SrTiO₃ layers on siliconwafers according to the present disclosure, further context for thedisclosure is provided in the following section by discussing severalmethods of removing native oxide layers and forming epitaxial SrTiO₃layers on silicon wafers, according to embodiments of the presentdisclosure. These embodiments are for example only and other methods canbe employed to form one or more layers of a ferroelectric oxide on aphotonic wafer.

FIGS. 1A-1F illustrate simplified cross-sectional views of steps,according to a method 200 described in FIG. 2, for forming a SrTiO₃layer on a silicon wafer, according embodiments of the disclosure.

As illustrated in FIG. 1A (step 205 of FIG. 2) a silicon wafer 105 thatincludes a layer of amorphous SiO₂ 110 is provided. In some embodimentssilicon wafer 105 can be between 500 microns and 1000 microns thick andcan have a single crystal structure.

As illustrated in FIG. 1B (step 210 of FIG. 2) a layer of Ge 115 isdeposited on layer of amorphous SiO₂ 110. In some embodiments layer ofGe 115 can be between 0.2 to 5 nanometers thick and can be deposited viaevaporation in molecular-beam epitaxy (MBE) chamber or other depositionprocess.

As illustrated in FIG. 1C (step 215 of FIG. 2) silicon wafer 105 can beheated to a temperature of 650-850° C. causing layer of Ge 115 to reactwith layer of amorphous SiO₂ 110 according to the reaction,Ge+SiO₂→Si+GeO. In one embodiment the temperature is between 700 and750° C., and in another embodiment is below 850° C. In furtherembodiments the temperature is below 800° C., below 750° C., or below700° C. In yet further embodiments the temperature is below 875° C.,below 900° C. or below 925° C. The resulting GeO is volatile causinglayer of SiO₂ 110 to be removed from the top surface of silicon wafer105.

As illustrated in FIG. 1D (step 220 of FIG. 2) the Ge deposition andsubsequent reaction with SiO₂ and desorption of GeO can be repeateduntil there is no SiO₂ remaining on the silicon. In some embodiments insitu real time monitoring of the SiO₂ remaining on the silicon surfacecan be used to determine if all of the SiO₂ has been removed and whetheranother Ge deposition and desorption process is needed. After the lastdesorption process is completed, in some embodiments residual Ge 120remains on the surface of silicon wafer 105 and may be randomlydistributed across the silicon surface.

As illustrated in FIG. 1E (step 225 of FIG. 2) a layer of epitaxialSrTiO₃ 125 is deposited on the surface of silicon wafer 105. In someembodiments layer of SrTiO₃ 125 is between 0.8 nanometers and 60nanometers thick and can be deposited using MBE. In various embodimentsother thicknesses can be used. In some embodiments a Ge effusion cellcan be located in a MBE tool that combines the de-oxidation and SrTiO₃growth in the same tool to reduce cost and to reduce the likelihood ofwafer contamination. In further embodiments, epitaxial BaTiO₃ can bedeposited instead of SrTiO₃.

As illustrated in FIG. 1F (step 230 of FIG. 2) silicon wafer 105 isexposed to molecular oxygen, atomic oxygen, or ozone at a temperatureabove 600° C. such that the oxygen permeates SrTiO₃ layer 125 andoxidizes residual Ge 120 that was randomly distributed across thesilicon surface. This converts residual Ge 120 to amorphousSi_(1-x)Ge_(x)O₂ 130 which is non-uniformly distributed bothhorizontally across silicon wafer 105 and vertically within theamorphous Si_(1-x)Ge_(x)O₂ layer, based on the location andconcentration of the residual Ge that was randomly distributed acrossthe silicon surface. The composition of Si_(1-x)Ge_(x)O₂ layer 130 canalso vary due to inter-diffusion of the Si_(1-x)Ge_(x)O₂ and thesilicon. The resulting Si_(1-x)Ge_(x)O₂ layer 130 is transparent atcertain wavelengths that may be suitable for use in lasers, including1550 nanometers.

In other embodiments residual Ge 120 that is randomly distributed acrossthe silicon surface as shown in FIG. 1E can be oxidized by other speciessuch as, but not limited to, wet oxygen, oxygen plasma and ozone. Infurther embodiments one or more post oxidation treatments can beemployed to improve the Si_(1-x)Ge_(x)O₂ quality and interfaces, asneeded.

In some embodiments a ferroelectric oxide such as, but not limited to,BaTiO₃, (Ba,Sr)TiO₃ (BST), (Pb(Zr,Ti)O₃ (PZT), (Pb, La)(Zr,Ti)O₃ (PLZT),(Sr,Ba)Nb₂O₆ (SBN) or LiNbO₃ can be grown on the SrTiO₃ layer usingmyriad deposition techniques, including but not limited to, MBE, CVD,PVD, PLD or sol gel. The resulting stack, ferroelectricoxide/SrTiO₃/Si_(1-x)Ge_(x)O₂/Si can be transparent to certainwavelengths of light, including 1550 nanometers, making the structureuseful, for example, for optical switches and waveguides. In yet furtherembodiments, the aforementioned post oxidation process can be employedafter a ferroelectric layer is grown on the SrTiO₃/Si_(1-x)Ge_(x)O₂/Sistack.

It will be appreciated that process 200 is illustrative and thatvariations and modifications are possible. Steps described as sequentialmay be executed in parallel, order of steps may be varied, and steps maybe modified, combined, added or omitted. As would be appreciated by oneof skill in the art the term “oxide” as used herein can refer to anypermutation of an oxide including but not limited to monoxide, dioxideor trixoide.

FIGS. 3A-3D illustrate simplified cross-sectional views of steps,according to a method 400 described in FIG. 4, for forming a SrTiO₃layer on a silicon wafer, according embodiments of the disclosure. Asshown in FIG. 4, method 400 uses a similar process as method 200,however before step 225 in method 200 in which the layer of SrTiO₃ isdeposited, in method 400 a layer of Ge is deposited in step 405 tocreate a graded layer. The graded layer changes composition such that atthe silicon surface the lattice has a higher percentage of silicon andhas therefore closely matches the lattice of the silicon wafer andtransitions to a higher percentage of Ge at the top of the layer andtherefore closely matches the lattice of the subsequent SrTiO₃ layer, asdescribed in more detail below.

As shown in FIG. 4, method 400 uses the same steps 205-220 as describedin FIG. 2 to form a wafer that is free from amorphous SiO₂ and hasresidual Ge randomly scattered across silicon surface 300. Therefore,FIG. 3A shows a silicon wafer 105 that has residual Ge 120 randomlyscattered across silicon surface 300 which results after performingsteps 205-220 of FIG. 4.

As illustrated in FIG. 3B (step 405 of FIG. 4) an epitaxial layer of Ge305 is grown on surface 300 of silicon wafer 105. In some embodimentslayer of Ge 305 is between 5 to 30 nanometers thick. In someembodiments, layer of Ge 305 can be converted to a graded layer thatchanges from a low concentration of Ge at silicon surface 300 to a highconcentration of Ge at top surface 310 of the Ge layer. In variousembodiments the conversion to a graded layer is performed by diffusingGe layer 305 and silicon wafer 105 together by exposing the wafer to atemperature between 600 and 900° C. After the diffusion process a gradedSi_(1-x)Ge_(x) layer is formed having a Ge concentration that variesfrom 0 atomic percent Ge within the bulk silicon to 100 atomic percentGe at top surface 310 of the graded Si_(1-x)Ge_(x) layer. In otherembodiments, the graded layer can vary from 0 atomic percent Ge withinthe bulk silicon to between 30% to 40% (x from 0.3 to 0.4) atomicpercent Ge at top surface 310 of the graded Si_(1-x)Ge_(x) layer. One ofskill in the art with the benefit of this disclosure would appreciatethat other concentration gradients can be formed.

In further embodiments, instead of forming a graded Ge and Si layer bydiffusing the Ge layer into the silicon, the graded Si_(1-x)Ge_(x) layercan be formed on the silicon via co-evaporation of Ge and Si using Geand Si effusion cells. During co-evaporation, the Si:Ge ratio can beadjusted as growth proceeds by changing the flux temperatures of each ofthe Si and Ge effusion cells.

In some embodiments the graded Si_(1-x)Ge_(x) layer has a larger latticeconstant than Si (40 percent Ge at Si_(1-x)Ge_(x) surface resulting inapproximately a 100 percent improvement in lattice match to the SrTiO₃layer), leading to a high quality SrTiO₃ layer that is subsequentlyformed on the graded layer, as described below.

As illustrated in FIG. 3C (step 410 of FIG. 4) an epitaxial layer ofSrTiO₃ 320 can be subsequently deposited on graded Ge layer 315. In someembodiments layer of SrTiO₃ 320 is between 0.8 to 60 nanometers thickand can be deposited using MBE. In other embodiments, epitaxial BaTiO₃can be grown directly on Si_(1-x)Ge_(x) layer 315 using MBE.

As illustrated in FIG. 3D (step 415 of FIG. 4) the wafer is exposed tomolecular oxygen, atomic oxygen, or ozone at a temperature above 600° C.such that the oxygen permeates SrTiO₃ layer 320 and oxidizes gradedSi_(1-x)Ge_(x) layer 315 (see FIG. 3C), forming a Si_(1-x)Ge_(x)O₂ layer325 that is transparent to certain wavelengths of light, including 1550nanometers. Therefore the entire stack can be useful, for example, foroptical switches and waveguides. As described above with regard to FIGS.1A-1D and method 200 in FIG. 2, in some embodiments one or morealternative oxidation processes can be used, different ferroelectricoxides can be deposited on the graded layer and optional post oxidationprocesses can also be used.

It will be appreciated that process 400 is illustrative and thatvariations and modifications are possible. Steps described as sequentialmay be executed in parallel, order of steps may be varied, and steps maybe modified, combined, added or omitted.

FIGS. 5A-5F illustrate simplified cross-sectional views of steps,according to a method 600 described in FIG. 6, for forming a SrTiO₃layer on a silicon wafer, according embodiments of the disclosure. Asshown in FIG. 6, method 600 starts with a silicon wafer 505 having aSiGe layer 510 terminated with a SiGeO₂ surface layer 515 that isremoved before a layer of SrTiO₃ is deposited, as described in moredetail below.

As illustrated in FIG. 5A (step 605 of FIG. 6) a silicon wafer 505includes an epitaxial Si_(1-x)Ge_(x) layer 510 terminated with a nativeoxide layer of amorphous SiGeO₂ 515. In various embodimentsSi_(1-x)Ge_(x) layer 510 can be graded (e.g., can change concentrationvertically within the layer as described in previous embodiments herein)while in other embodiments the Si_(1-x)Ge_(x) layer can be of uniformconcentration. In some embodiments silicon wafer 505 can be between 500microns and 1000 microns thick and can have a single crystal structure.

As illustrated in FIG. 5B (step 610 of FIG. 6) a layer of Ge 520 isdeposited on SiGeO₂ layer 515. In some embodiments layer of Ge 520 canbe between 0.2 to 5 nanometers thick and can be deposited via anevaporation or other deposition process.

As illustrated in FIG. 5C (step 615 of FIG. 6) the wafer can be heatedto a temperature >650° C. causing layer of Ge 520 to react with layer ofSiGeO₂ 515 according to the reaction, Ge+SiO₂→Si+GeO. In someembodiments the temperature may be different as described in step 215 ofFIG. 2. The resulting GeO is volatile causing at least a portion oflayer of SiGeO₂ 515 to be desorbed from the surface of silicon wafer505.

As illustrated in FIG. 5D (step 620 of FIG. 6) the Ge deposition,subsequent reaction with SiO₂ and desorption of GeO can be repeateduntil there is no SiGeO₂ remaining on the wafer. In some embodiments insitu real time monitoring of the SiGeO₂ remaining on the wafer surfacecan be used to determine if all of the SiGeO₂ has been removed andwhether additional Ge deposition and desorption processes are needed.After the last desorption process is completed, the wafer has an oxidefree top surface 520 of layer of Si_(1-x)Ge_(x) 510.

As illustrated in FIG. 5E (step 625 of FIG. 6) a layer of epitaxialSrTiO₃ 525 is deposited on layer of Si_(1-x)Ge_(x) 510. In someembodiments layer of SrTiO₃ 525 is between 0.8 and 60 nanometers thickand can be deposited using MBE or another suitable deposition process.

As illustrated in FIG. 5F (step 630 of FIG. 6) the wafer is exposed tomolecular oxygen, atomic oxygen, or ozone at a temperature above 600° C.such that the oxygen permeates layer of SrTiO₃ 525 and oxidizes theunderlying layer of Si_(1-x)Ge_(x) 510. The oxygen converts layer ofSi_(1-x)Ge_(x) 510 to a layer of Si_(1-x)Ge_(x)O₂ 530 which istransparent at certain wavelengths that may be suitable for use inlasers, including 1550 nanometers. As described above with regard toFIGS. 1A-D and method 200, in some embodiments one or more alternativeoxidation processes can be used, different ferroelectric oxides can bedeposited on layer of Si_(1-x)Ge_(x) 510, and alternative post oxidationprocesses can also be used.

It will be appreciated that process 600 is illustrative and thatvariations and modifications are possible. Steps described as sequentialmay be executed in parallel, order of steps may be varied, and steps maybe modified, combined, added or omitted.

In the foregoing specification, embodiments of the disclosure have beendescribed with reference to numerous specific details that can vary fromimplementation to implementation. The specification and drawings are,accordingly, to be regarded in an illustrative rather than a restrictivesense. The sole and exclusive indicator of the scope of the disclosure,and what is intended by the applicants to be the scope of thedisclosure, is the literal and equivalent scope of the set of claimsthat issue from this application, in the specific form in which suchclaims issue, including any subsequent correction. The specific detailsof particular embodiments can be combined in any suitable manner withoutdeparting from the spirit and scope of embodiments of the disclosure.

Additionally, spatially relative terms, such as “bottom or “top” and thelike can be used to describe an element and/or feature's relationship toanother element(s) and/or feature(s) as, for example, illustrated in thefigures. It will be understood that the spatially relative terms areintended to encompass different orientations of the device in use and/oroperation in addition to the orientation depicted in the figures. Forexample, if the device in the figures is turned over, elements describedas a “bottom” surface can then be oriented “above” other elements orfeatures. The device can be otherwise oriented (e.g., rotated 90 degreesor at other orientations) and the spatially relative descriptors usedherein interpreted accordingly.

What is claimed is:
 1. A method for processing a substrate, the methodcomprising: positioning the substrate in a deposition chamber, whereinthe substrate comprises a wafer of single crystal silicon covered with alayer of amorphous silicon oxide; depositing a layer of germanium on thelayer of amorphous silicon oxide; and heating the substrate to atemperature below 850° C. causing at least a portion of the layer ofamorphous silicon oxide to react with the layer of germanium to formgermanium oxide.
 2. The method of claim 1 further comprising repeatingthe depositing the layer of germanium and the heating the substrateuntil the layer of amorphous silicon oxide is removed from the wafer ofsingle crystal silicon.
 3. The method of claim 2 wherein after theamorphous silicon oxide is removed from the wafer of single crystalsilicon, residual germanium from the depositing the layer of germaniumis distributed on the wafer of single crystal silicon.
 4. The method ofclaim 3 further comprising depositing an epitaxial layer of strontiumtitanate on the wafer of single crystal silicon and on the residualgermanium.
 5. The method of claim 4 further comprising exposing thewafer of single crystal silicon to oxygen after the depositing theepitaxial layer of strontium titanate, causing the silicon and theresidual germanium to react forming a silicon germanium oxide layerbetween the layer of strontium titanate and the wafer of single crystalsilicon.
 6. The method of claim 2 further comprising depositing a layerof germanium on the wafer of single crystal silicon after the layer ofamorphous silicon oxide is removed.
 7. The method of claim 6 furthercomprising exposing the layer of germanium and the wafer of singlecrystal silicon to a temperature sufficient to cause the layer ofgermanium to inter-diffuse with the wafer of single crystal silicon tocreate a graded layer having a composition higher in silicon thangermanium at the wafer of single crystal silicon and a composition thatis higher in germanium than silicon at a top of the graded layer.
 8. Themethod of claim 2 further comprising depositing a graded layer on thewafer of single crystal silicon after the layer of amorphous siliconoxide is removed, the graded layer having a composition higher insilicon than germanium at the wafer of single crystal silicon and acomposition that is higher in germanium than silicon at a top of thegraded layer.
 9. A method for removing an oxide layer from a substrate,the method comprising: depositing a layer of germanium on the oxidelayer; and heating the substrate to a temperature below 850° C. to causethe layer of germanium to react with the oxide layer and generategermanium oxide.
 10. The method of claim 9 wherein the substratecomprises silicon and the oxide layer comprises silicon dioxide.
 11. Themethod of claim 9 wherein the substrate comprises silicon germanium andthe oxide layer comprises silicon germanium dioxide.
 12. The method ofclaim 9 wherein the temperature is between 700° C. and 750° C.
 13. Themethod of claim 9 further comprising repetitively depositing the layerof germanium and heating the substrate until the oxide layer is removed.14. The method of claim 13 further comprising depositing germanium on asurface of the substrate after the oxide layer is removed.
 15. Themethod of claim 14 further comprising depositing an epitaxial layer ofstrontium titanate after the depositing the germanium.
 16. The method ofclaim 15 further comprising exposing the substrate to oxygen after thedepositing the epitaxial layer of strontium titanate, the oxygen causingthe germanium to form a layer of silicon germanium oxide between thesubstrate and the epitaxial layer of strontium titanate.
 17. A methodfor processing a substrate, the method comprising: positioning thesubstrate in a deposition chamber, wherein the substrate comprises a toplayer of silicon germanium oxide, a middle layer of silicon germaniumand a bottom layer of silicon; depositing a layer of germanium on thelayer of silicon germanium oxide; and heating the substrate to atemperature below 850° C. causing at least a portion of the layer ofsilicon germanium oxide to react with the layer of germanium to formgermanium oxide.
 18. The method of claim 17 further comprising repeatingthe depositing the layer of germanium and the heating the substrateuntil the layer of silicon germanium oxide is removed from the layer ofsilicon germanium.
 19. The method of claim 18 further comprisingdepositing an epitaxial layer of strontium titanate on the layer ofsilicon germanium.
 20. The method of claim 19 further comprisingexposing the layer of strontium titanate to oxygen causing the layer ofsilicon germanium to react with the oxygen forming a layer of silicongermanium oxide between the layer of strontium titanate and the layer ofsilicon.